BITUMEN GRADES AND SPECIFICATION
Bitumen grade 60/70 | ||
TEST METHOD | SPECIFICATION | TEST |
D - 70 | 1.01 - 1.06 | SPECIFIC GRAVITY @25/25 C |
D - 5 | 60/70 | PENETRATION @25 C |
D - 36 | 49/56 | SOFTENING POINT C |
D - 113 | 100 MIN | DUCTILITY@25 C |
D - 6 | 0.2 MAX | LOSS ON HEATING (WT)% |
D - 6 & D - 5 | 20 MAX | DROP IN PENETRATION AFTER HEATING % |
D - 92 | 250 MIN | FLASH POINT C |
D - 4 | 99.5 MIN | SOLUBILITY IN CS2 (WT)% |
* A.A.S.H.O.T.102 | NEGATIVE | SPOT TEST |
آنالیز وکیوم باتوم
RESALT | TEST METHOD | TEST | NO |
1.189 | ASTM –D3289 | Specific gravity @ 25/25 C 0 | 1 |
3 | ASTM –D5 | PENETRATION @ 25C0 , 10-1 | 2 |
76.5 | ASTM –D36 | SOFTENING POINT. C0 | 3 |
0.5 | ASTM –D113 | DUCTILITY@ 25 C0 ,CM | 4 |
------ | ASTM –D6 | LOOS ON HEALTING, WT% | 5 |
------ | ASTM –D5/D6 | HEAFING% | 6 |
------ | ASTM –D92 | FLASH POINT C0 | 7 |
69.3 | ASTM –D-4 | SOLU BILITY IN CS2, WT% | 8 |
10.6 | ASTM –D482 | ASH CONTENT WT% | 9 |